    Investigation of mechanical and durability properties of brick powder-added White Cement composites with three different fibers
    (ELSEVIER SCI LTD, THE BOULEVARD, LANGFORD LANE, KIDLINGTON, OXFORD OX5 1GB, OXON, ENGLAND, 2022) Alcharchafche, Mahmood Anwar Shaker; Al-Mashhadani, Mukhallad M.; Aygörmez, Yurdakul
    Traditional Portland Cement is used extensively in the construction industry today. Portland Cement has a gray color and has been explored with numerous substitutes. With the increasing interest in concrete technology, the interest in composite materials with higher performance and strength has gained more importance. White Cement (WC) is an important cement type in this field. However, studies of substitute materials for White Cement are limited and more research is needed. In this study, while White Cement and clay brick powder (CBP) were substituted at three different rates (5%, 10%, and 15%), three different fibers (copper-coated (CC) steel fiber, crimped (C) steel fiber, and basalt (B) fiber) were used at the ratio of 0.4% to examine the effect of fibers at the same time. The compressive and flexural strengths of the prepared series were investigated for 28 and 90 days. Three different durability tests were applied after 90 days: elevated-temperature test (250, 500, and 750 ?C), freezing-thawing test (90 cycles), and sulfate effect (90 days). Following the durability tests, weight and strength values were compared. In addition, SEM and XRD analyzes were made while making comparisons before and after the durability test of the samples and a visual examination was made in the durability conditions. The use of 5% brick powder increased the strength values due to the formation of C-A-S-H and C-S-H gels due to its higher Al2O3 and SiO2 content, while the use of higher brick powder caused a decrease in strength. While the fibers contributed positively to the strength values, the highest increase was in the longer crimped steel fiber added sample and the lowest increase was in the shorter copper-coated steel fiber added sample. While there was a 13% increase in compressive strength in the crimped steel fiber and 5% brick dust added sample compared to the control sample, there was a 21% increase in flexural strength. As a result of the durability tests, the samples behaved in similar order and maintained their stability despite significant losses.
  • Küçük Resim
    Öğe
    Tuğla tozu katkılı beyaz çimentolu kompozitlerin mekanik ve durabilite özelliklerinin araştırılması
    (İstanbul Gelişim Üniversitesi Lisansüstü Eğitim Enstitüsü, 2022) Alcharchafche, Mahmood Anwar Shaker
    Bu tez çalışması, tuğla tozu atığının kısmen karışıma dahil edildiği Beyaz Çimento harcının özelliklerinde meydana gelen değişiklikleri incelemeyi amaçlamaktadır. Beyaz Çimentoya %5, %10 ve %15 oranlarındaki tuğla tozu ikameleri yapılmış olup, ayrıca %0,4 oranında lif katkıları (pirinç kaplı çelik lifler, zikzaklı çelik lifler ve bazalt lifler) eklenmiştir. Kullanılan karışımların avantaj ve dezavantajlarını doğrulamak maksadıyla bu numunelerin basınç dayanımı ve eğilme dayanımı araştırılmıştır. Ayrıca 90 gün sonra numunelere yüksek sıcaklık, donma-çözülme ve sülfat etkileri uygulanmış ve fiziksel ve mekanik özelliklerindeki değişiklikler araştırılmıştır. Genel olarak, sonuçlar; tuğla tozunun ilave edilmesinin, karışımın basınç ve eğilme dayanımını artıracağını, bu yüzden kullanılmasının faydalı olacağını, ancak -karışımın homojenliğine zarar vermemek ve basınç ve eğilme dayanımının azalmaması adına- ilave oranının %5 ile sınırlı tutulmasının uygun olacağını göstermektedir. Lifli serilerde sonuçların olumlu yönde iyileşeceği görülmüştür. En yüksek artışların zikzaklı çelik liflerde olduğu görülürken en düşük artışların pirinç kaplı çelik liflerde olduğu görülmüştür. Durabilite testlerinden sonraki sonuçlarda azalmalar görülürken sonuçların sıralaması durabilite testleri öncesine paralellik göstermiştir.